Hardener For Epoxy Resin(Modified Polyamines)
Grade |
Viscosity |
AmineValue |
THEO
A.H.E.W☆ |
Gardner Colour |
Compounding Ratio |
Sp. Gr. |
Gel Time |
Characteristics & Application |
400~700 |
305±15 |
92 |
15 Max. |
45~55 |
1.12 |
15 Min. |
Solvent-less Paint | |
FUJICURE 4200 |
1,700~2,700 |
370±15 |
100 |
3 Max. |
50~60 |
0.97 |
110 Min. |
Casting(Light colour. Anti-weathering) |
650~900 |
380±15 |
80 |
2 Max. |
35~55 |
0.95 |
50 Min. |
Modified cycloaliphatic amine. Lining(Anti-weathering) |
|
800~2,500 |
365±15 |
100 |
4 Max. |
50~70 |
1.02 |
65 Min. |
Flooring material. Primer for lining.(Wet surface type) |
|
3,500~7,500 |
395±15 |
95 |
2 Max. |
40~70 |
1.08 |
50 Min. |
Paint(Good corrosion resistance) |
|
1,000~2,000 |
325±15 |
120 |
5 Max. |
50~70 |
1.10 |
70 Min. |
Paint. Lining. |
|
6,000~14,000 |
270±10 |
140 |
4 Max. |
60~80 |
1.10 |
11 Min. |
Lining.Flooring material(Low temperature.Fast curing type) |
|
1,000~2,000 |
340±15 |
110 |
4 Max. |
50~70 |
1.03 |
35 Min. |
Epoxy mortar. |
|
800~1,700 |
395±20 |
95 |
9 Max. |
40~70 |
1.02 |
60 Min. |
Low cost type of FUJICURE 5000. Lining. Flooring material. |
|
40~70 |
305±15 |
92 |
3 Max. |
40~50 |
0.95 |
93 Min. |
Adhesive. Casting. Coatings. Flooring material. |
|
300~700 |
270±10 |
115 |
1 Max. |
50~70 |
1.03 |
45 Min. |
Modified cycloaliphatic amine. Solvent-free coatings. Self-leveling Floor and mortars. Good colour stability and hight gloss. |
|
1,000~1,400 |
275±10 |
98 |
12 Max. |
45~55 |
1.16 |
43 Min. |
Casting. Laminates. Tar / Epoxy coatings. Floor. Excellent chemical resistance. Low temperature cure. A very stable hardener mix of any desired degree of reactivity or pot life can be obtained by mixing FXM-824A with FXM-824B |
|
2,500~3,500 |
290±10 |
95 |
15 Max. |
45~55 |
1.13 |
20 Min. |
||
2,000~3,000 |
290±10 |
95 |
15 Max. |
45~55 |
1.12 |
720 Min. |
||
2,000~5,000 |
375±20 |
80 |
5 Max. |
30~50 |
1.05 |
18 Min. |
Civil engineering.(Low temperature, wet surface curing type) Coatings. Lining. Adhesive. |
|
FUJICURE FX-220 |
1,000~2,000 |
370±20 |
80 |
5 Max. |
30~50 |
1.05 |
22 Min. |
Civil engineering.(Low temperature, wet surface curing type) Coatings. Adhesive. |
☆THEO.A.H.E.W=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT) The physical properties of the cured epoxy resin system will change with different mixed ratio of the hardener. The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory. |
|
|||||||