Hardener For Epoxy Resin(Solution types)
Grade
|
Base Resin
|
Resin Content
|
Solvent(ratio) |
Amine Value |
THEO. A.H.E.W☆ |
Gardner Colour |
Solution Viscosity |
Compounding Ratio |
Characteristics & Application
|
KINGMIDE 300 |
65±2 |
xylene/lsobutanolm
( 70 / 30 ) |
63±5 |
750 |
9
Max. |
Z1-Z6 |
130~170(1) |
Curing agent for solid epoxy coating, fast dry, good adhesion primers. |
|
KINGMIDE 150-50 |
KINGMIDE 300
|
50±2 |
xylene/lsobutanolm ( 70 / 30 ) |
48±5 |
950 |
9
Max. |
S-W |
160~220(1)
|
Curing agent for solid epoxy coating, fast dry, good adhesion primers. |
KINGMIDE 305
|
60±2 |
xylene/lsobutanolm ( 70 / 30 ) |
150±10 |
300 |
9 Max. |
L-R |
50~70(1) |
Paint (general, zinc-rich, tar) good corrosion resistance. |
|
KINGMIDE 305
|
70±2 |
xylene/lsobutanolm ( 70 / 30 ) |
170±10 |
255 |
9 Max. |
W-Z |
40~60(1) |
Paint (general, zinc-rich, tar) good corrosion resistance. | |
KINGMIDE 315-80 |
KINGMIDE 315
|
80±2 |
xylene/lsobutanolm ( 70 / 30 ) |
270±20 |
150 |
9 Max. |
X-Z |
25~35(1) |
Water resistance, high performance epoxy paint, tar epoxy, fast dry. |
60±2
|
xylene/lsobutanolm ( 80 / 20 ) |
210±15 |
150 |
9 Max. |
H-N |
20~35(1) 70~90(2) |
Paint (fast curing type). | ||
60±2 |
xylene/lsobutanolm ( 80 / 20 ) |
145±10 |
255 |
9 Max. |
Z-Z3 |
50~70(1) |
Paint (fast curing type) |
||
75±2 |
xylene ( 100 ) |
250±15 |
130 |
9
Max. |
Z-Z5 |
20~30(1) 70~90(2) |
Paint (fast curing type) | ||
|
☆THEO.A.H.E.W.=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT) THE physical prpperties of the cured epoxy resin system will change with different mixed ratio of the hardener. The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory. |
|
||||||||