Hardener For Epoxy Resin(Polyaminoamide)

　

Grade
Viscosity
AmineValue
THEO A.H.E.W ☆
Gardner Colour
Compounding Ratio
Sp. Gr.
Gel Time
Characteristics & Application
KINGMIDE 300
200~600 / 200
97±5
500
10 Max.
100(1)
0.97
—
Solvent Based Coatings with Solid Epoxy Resins have Fast Tack Free Time and Good Flexibility, Hot Melt Adhesives.
50,000~70,000 / 40
240±15
180
10 Max.
36(1)   100(2)
0.97
130 Min.(2)
Coatings, Adhesive for Abrasive Materials, Tar Epoxy and Plasticizer
30,000~50,000 / 40
250±15
170
10 Max.
34(1)    90(2)
0.97
100 Min.(2)
Coatings, Adhesive for Abrasive Materials, Tar Epoxy and Plasticizer.

8,000~12,000 / 40
335±15

120
10 Max.

25(1)    67(2)
0.97
150 Min.(2)
General Adhesive, Coating, Casting, Potting.
8,000~12,000 / 40
335±15

120
11 Max.
25(1)    67(2)
0.97
110 Min.(2)
General Adhesive, Faster Curing Time than #315.

1,500~3,000 / 25
440±20

85
10 Max.
50(2)

0.97
80 Min.(2)
General Adhesive, Civil Engineering and Construction, Molding.

10,000~20,000 /25
380±20

95
10 Max.

50(2)
0.97
120 Min.(2)
General Adhesive, Civil Engineering and Construction, Toughness.
450~650 / 25

610±20

60
10 Max.
33(2)
0.96
20 Min.(2)
Solvent-less, Lining, Casting, Flooring Material
400~600 / 25

790±20
60
12 Max.
33(2)
0.96
30 Min.(2)
Solvent-less, Lining, Grouting.
2,500~4,500 / 25
350±20

110
12 Max.

50(2)
0.95
100 Min.(2)
Civil Engineering, Casting, Adhesive
500~1,000 / 25
350±20
110
12 Max.
50(2)

0.95
200 Min.(2)
Civil Engineering, Casting, Adhesive
200~400 / 25
410±20
100
12 Max.
50(2)
0.96
70 Min.(2)
Civil Engineering and Construction, Epoxy Mortar.
200~400 / 25
550±20
65
12 Max.
33(2)
0.95
40 Min.(2)
Civil Engineering and Construction, Epoxy Mortar.
6,000~12,000 / 25
350±20
110
10 Max.
50(2)
1.04
50 Min.(2)
Low Temperature Cure, Under Water Cure, Adhesive, Lining Colour Stable System.
450~600 / 25
330±15
90
10 Max.
50(2)
1.01
42 Min.(2)
Epoxy Motar, Cures under humid conditions and low temperature.
11000/ 25
202
—
6~7
—
0.983
—
polyaminoamide, is a product to provide good adhesive property of plasticized PVC-sol.

☆THEO A.H.E.W.=(THEORETICAL ACTIVE HYDROGEN EQUIVALENT WEIGHT)

The physical properties of the cured epoxy resin system will change with different mixed ratio of the hardener.

The value listed on the above table is the average value of many datas which are obtained by the different physical properties test at the ambient temperature in the laboratory.

  1. The parts of Hardener by weight to 100 parts of Epoxy Resin(EEW:450~500)

  2. The parts of Hardener by weight to 100 parts of Epoxy Resin(EEW:180~200)

  3. Brookfield RVT Type; 1mPa.s.=1cP。

  4. Gel Time : Total amount 100g at 20~23℃。

  5. ※ Total amount 200g at 20~23℃ Softening Point : The Softening Point of KINGMIDE 210 is 45℃ determined by Ball-and-Ring method.